About This Item
Description
Jet Lube KOPR KOTE 10041 Copper/Graphite High-Temp Anti-Seize (MIL-PRF-907E) 12 oz Aerosol
- Not classified as marine pollutant - DOT Approval CA2004080025
- NSF Registered H2 (No. 120923)
- Conforms to MIL-PRF-907E
- Service rating: -65Deg F (-54Deg C) to 1800Deg F (982Deg C).
- Contains no lead or zinc.
- Lowers friction; reduces wrench torque.
- Permits reuse of fittings; saves stud, bolt, and nut replacement.
- Aluminum complex base for brushability and stability over a wide temperature range.
- Not affected by contraction, expansion, or vibration.
- Will not run, drip, or settle out.
- Available in convenient aerosol form
KOPR-KOTE Aerosol is a low-friction, anti-seize lubricant manufactured from a combination of micro-size copper flakes and graphite dispersed in a water-resistant grease and fortified with antioxidants, plus rust and corrosion inhibitors. KOPR-KOTE Aerosol offers quick recovery of performance through the rapid evaporation of propellant and solvent. KOPR-KOTE provides a shield against metal-to-metal contact, preventing seizure and corrosion. It fills irregularities and imperfections and resists welding, hardening, or setting. KOPR-KOTE provides low friction and cushions impact and shock loads. Low shear between particles reduces stick-slip, allowing quick disassembly with minimum wrench torque. It will not squeeze out of the threads, gum up or wash off. Size: 12 oz
- Thickener Aluminum Complex
- Fluid Type Petroleum
- Dropping Point (ASTM D-566) 450Deg F (232Deg C)
- Specific Gravity 1.10
- Density (lb/gal) 9.20
- Oil Separation (ASTM D-6184) <3.0
- WT. % LOSS @ 212Deg F (100Deg C)
- Flash Point (ASTM D-92) >140Deg F (60Deg C)
- K-Factor .15
- 1" B7 Studs @ 80,000 psi Contact Stress
- NFPR 30B Level II
- Spray Pattern 2 - 4" Cone
- 4-Ball (ASTM D-2596)
- Weld Point, kgf 800
- Load Wear Index 125
- Propellant type Hydrocarbon